96946. Constructional Steel 43crmo4 1.3563 Bar& Rod for General Engineering Purposes 
[Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 43CrMo4 1.3563 bar& rod] Introduction: Heat treated : 1898°C - 1252°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96947. Constructional Steel 48crmo4 1.3565 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 48CrMo4 1.3565 bar& rod] Introduction: Heat treated : 1924°C - 1334°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96948. Constructional Steel 50mnsi4 1.5131 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 50MnSi4 1.5131 bar& rod] Introduction: Heat treated : 1138°C - 1545°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96949. Constructional Steel 36nicr6 1.5710 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 36NiCr6 1.5710 bar& rod] Introduction: Heat treated : 1138°C - 1545°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96950. Constructional Steel 35nicr18 1.5864 Rod & Bar for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 35NiCr18 1.5864 bar& rod] Introduction: Heat treated : 1675°C - 1941°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96951. Constructional Steel 38cr2 1.7003 Rod & Bar for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 38Cr2 1.7003 bar& rod] Introduction: Heat treated : 1282°C - 1173°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96952. Constructional Steel 46cr2 1.7006 Rod & Bar for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 46Cr2 1.7006 bar& rod] Introduction: Heat treated : 1987°C - 1868°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96953. Constructional Steel 34cr4 1.7033 Rod & Bar for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 34Cr4 1.7033 bar& rod] Introduction: Heat treated : 1553°C - 1223°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96954. Constructional Steel 37crs4 1.7038 Rod & Bar for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 37CrS4 1.7038 bar& rod] Introduction: Heat treated : 1284°C - 1876°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96955. Constructional Steel 34crs4 1.7037 Rod & Bar for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 34CrS4 1.7037 bar& rod] Introduction: Heat treated : 1656°C - 1925°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96956. Constructional Steel 41crs4 1.7039 Rod & Bar for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 41CrS4 1.7039 bar& rod] Introduction: Heat treated : 1543°C - 1798°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96957. Constructional Steel 34CrMo4 1.7220 Rod & Bar for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 34CrMo4 1.7220 bar& rod] Introduction: Heat treated : 1719°C - 1937°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96958. Constructional Steel 42CrMo4 1.7225 Rod & Bar for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 42CrMo4 1.7225 bar& rod] Introduction: Heat treated : 1918°C - 1111°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96959. Constructional Steel 42crmos4 1.7227 Rod & Bar for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 42CrMoS4 1.7227 bar& rod] Introduction: Heat treated : 1867°C - 1228°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section ...
Company: Wuxi Taixie Metal Material Co., Ltd.
96960. Constructional Steel 1.3501 100cr2w1 Rod & Bar Ball Bearing Steels [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 1.3501 100Cr2W1 bar& rod] Introduction: Heat treated : 1443°C - 1668°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section ...
Company: Wuxi Taixie Metal Material Co., Ltd.