Jiangsu Profile
Product List
1696. Steel C55 1.0535 S55c 1055 Bar& Rod for General Engineering 
[Jul 29, 2024]
[Jul 29, 2024] 1.[ C55 1.0535 S55C 1055 bar& rod ] Standard: EN 10277-2: 2008 Bright steel products. Technical delivery conditions. Steels for general engineering purposes EN 10083-2: 2006 Steels for quenching ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1697. Constructional Steel 23crmob33 1.7271 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 23CrMoB33 1.7271 bar& rod] Introduction: Heat treated : 1618°C - 1519°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1698. Constructional Steel 20crmo2 1.7311 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 20CrMo2 1.7311 bar& rod] Introduction: Heat treated : 1963°C - 1536°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1699. Constructional Steel 20mocrs4 1.7323 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 20MoCrS4 1.7323 bar& rod] Introduction: Heat treated : 1627°C - 1119°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1700. Constructional Steel 25mocr4 1.7325 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 25MoCr4 1.7325 bar& rod] Introduction: Heat treated : 1696°C - 1433°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1701. Constructional Steel 25mocrs4 1.7326 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 25MoCrS4 1.7326 bar& rod] Introduction: Heat treated : 1696°C - 1433°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1702. Constructional Steel 34cral6 1.8504 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 34CrAl6 1.8504 bar& rod] Introduction: Heat treated : 1824°C - 1838°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1703. Constructional Steel 39crmov13.9 1.8523 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 39CrMoV13.9 1.8523 bar& rod] Introduction: Heat treated : 1532°C - 1186°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1704. Constructional Steel 60s20 1.0728 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 60S20 1.0728 bar& rod] Introduction: Heat treated : 1526°C - 1645°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1705. Constructional Steel C55 1.0535 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel C55 1.0535 bar& rod] Introduction: Heat treated : 1853°C - 1515°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1706. Constructional Steel C60 1.0601 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel C60 1.0601 bar& rod] Introduction: Heat treated : 1381°C - 1369°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1707. Constructional Steel 40mn4 1.1157 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 40Mn4 1.1157 bar& rod] Introduction: Heat treated : 1236°C - 1459°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1708. Constructional Steel 36mn5 1.1167 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel 36Mn5 1.1167 bar& rod] Introduction: Heat treated : 1944°C - 1864°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1709. Constructional Steel Cm35 1.1180 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel Cm35 1.1180 bar& rod] Introduction: Heat treated : 1229°C - 1224°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section on ...
Company: Wuxi Taixie Metal Material Co., Ltd.
1710. Constructional Steel Ck35 1.1181 Bar& Rod for General Engineering Purposes [Jul 29, 2024]
[Jul 29, 2024] 1.[ Constructional steel Ck35 1.1181 bar& rod] Introduction: Heat treated : 1623°C - 1661°C Yield Rp0.2 (MPa) Tensile Rm (MPa) Impact KV/Ku (J) Elongation A (%) Reduction in cross section ...
Company: Wuxi Taixie Metal Material Co., Ltd.